Ranges of Materials
Most Ceramics Sintered to Theoretical Density
Alumina No dopants
1700°C, 10 min in H2
Chromium Oxide doped
1700°C, 10 min in H2
Vanadium Oxide doped
1700°C, 10 min in H2
1100°C, 10 min
1800°C, 60 min in N2
WC/Co Cutting Tools
WC/Co/Diamond Based
Cutting Tools
WC/CO and Diamond Composites
Metal Powder Parts
Synthesis of Aligned Carbon Nano Tubes in H-Field
On Si substrate with Fe catalyst
in C2H2 Substrate Temperature,
700°C, Growth time, 5min.
Single Mode Cavity, 2.45 GHz
Microwave Growth of ZnO Microtubes
Grown by MW method
Single crystal form
Well Developed facets
Outer diameter from 50 to 200 mm
Wall thickness from 1 to 2 mm
Length from 2 to 5 mm
Applications
High Temperature Transistors
UV Light Detectors
Eleectrooptic Devices
Blue & UV Light Emitting Diodes (LEDs)
Blue & UV Lasers (LDs)
Microwave Brazing, Melting, and Coating of Metal Parts
Selective Heating of Powder